Material properties of isotropic bonded Nd-Fe-B magnets (NEOQUENCH-P)
Magnetic properties
Compression molded magnets
Compression mold NEOQUENCH-P, Magnetic property of NdFeB bonded magnet
NP-7L | NP-8 | NP-8L | ||
---|---|---|---|---|
Remanence, Br | (mT) | 570 ~ 640 | 580 ~ 650 | 640 ~ 710 |
(kG) | (5.7 ~ 6.4) | (5.8 ~ 6.5) | (6.4 ~ 7.1) | |
Coercivity, HCB | (kA/m) | 374 ~ 438 | 390 ~ 454 | 406 ~ 470 |
(kOe) | (4.7 ~ 5.5) | (4.9 ~ 5.7) | (5.1 ~ 5.9) | |
Coercivity, HCJ | (kA/m) | 637 ~ 796 | 1035 ~ 1353 | 637 ~ 796 |
(kOe) | (8.0 ~ 10.0) | (13.0 ~ 17.0) | (8.0 ~ 10.0) | |
Maximum energy product, (BH)max | (kJ/m3) | 56 ~ 68 | 60 ~ 72 | 68 ~ 80 |
(MGOe) | (7.0 〜 8.5) | (7.5 ~ 9.0) | (8.5 ~ 10.0) | |
Recoil permeability | 1.2 | 1.13 | 1.2 | |
Temperature coefficient of Br, alpha | (%/℃) | -0.12 | -0.15 | -0.1 |
Required magnetizing field for saturation, Hs | (kA/m) | ≧1592 | ≧1990 | ≧1592 |
(kOe) | (≧20) | (≧25) | (≧20) | |
Density | (Mg/m3) | 5.6 ~ 6.1 | 5.6 ~ 6.1 | 5.6 ~ 6.1 |
(g/cm3) | ||||
Method of forming | Compression moulding |
NP-8SR | NP-10LL | NP-11L | NP-12L | ||
---|---|---|---|---|---|
Remanence, Br | (mT) | 600 ~ 680 | 670~740 | 680 ~ 730 | 720 ~ 770 |
(kG) | (6.0 ~ 6.8) | (6.7~7.4) | (6.8 ~ 7.3) | (7.2 ~ 7.7) | |
Coercivity, HCB | (kA/m) | 414 ~ 486 | 398~462 | 430 ~ 485 | 454 ~ 509 |
(kOe) | (5.2 ~ 6.1) | (5.0~5.8) | (5.4 ~ 6.1) | (5.7 ~ 6.4) | |
Intrinsic Coercivity, HCJ | (kA/m) | 836〜1075 | 517~677 | 716 ~ 836 | 716 ~ 836 |
(kOe) | (10.5 ~ 13.5) | (6.5~8.5) | (9.0 ~ 10.5) | (9.0 ~ 10.5) | |
Maximum energy product, (BH)max | (kJ/m3) | 65 ~ 77 | 76~84 | 80 ~ 88 | 88 ~ 99 |
(MGOe) | (8.2 〜 9.7) | (9.5~10.5) | (10.0 ~ 11.0) | (11.0 ~ 12.5) | |
Recoil permeability | 1.13 | 1.26 | 1.2 | 1.2 | |
Temperature coefficient of Br, alpha | (%/℃) | -0.13 | -0.11 | -0.1 | -0.1 |
Required magnetizing field for saturation, Hs | (kA/m) | ≧1592 | ≧1592 | ≧1592 | ≧1592 |
(kOe) | (≧20) | (≧20) | (≧20) | (≧20) | |
Density | (Mg/m3) | 5.6 ~ 6.1 | 5.9~6.2 | 5.9 ~ 6.2 | 6.1 ~ 6.4 |
(g/cm3) | |||||
Method of forming | Compression moulding |
- R: Heat resistant
- SR: Super Heat resistant
- The data in these tables are obtained from Daido's standard test pieces and are not guranteed values.
- These values may vary depending on the magnet shape, dimensions, test conditions and equipment. It is recommended that the fiqures be verified in actual products.
- Guaranteed values may be set up by consultation for specific shape and sizes.
- The contents of data are subject to change without prior notice.
Injection molded magnets
Injection mold NEOQUENCH-P, Magnetic property of NdFeB bonded magnet
NPI-4L (NC-4L) |
NPI-6 (NC-6) |
NPI-6L (NC-6L) |
NPI-8L | ||
---|---|---|---|---|---|
Remanence, Br | (mT) | 410 ~ 490 | 480 ~ 560 | 540 ~ 620 | 570 ~ 630 |
(kG) | (4.1 ~ 4.9) | (4.8 ~ 5.6) | (5.4 ~ 6.2) | (5.7 ~ 6.3) | |
Coercivity, HCB | (kA/m) | 247 ~ 310 | 334 ~ 398 | 342 ~ 406 | 382 ~ 430 |
(kOe) | (3.1 ~ 3.9) | (4.2 ~ 5.0) | (4.3 ~ 5.1) | (4.8 ~ 5.4) | |
Intrinsic Coercivity, HCJ | (kA/m) | 573 ~ 732 | 1035 ~ 1353 | 637 ~ 796 | 676 ~ 835 |
(kOe) | (7.2 ~ 9.2) | (13.0 ~ 17.0) | (8.0 ~ 10.0) | (8.5 ~ 10.5) | |
Maximum energy product, (BH)max | (kJ/m3) | 28 ~ 36 | 40 ~ 52 | 49 ~ 61 | 59 ~ 67 |
(MGOe) | (3.5 ~ 4.5) | (5.0 ~ 6.5) | (6.2 ~ 7.7) | (7.4 ~ 8.4) | |
Recoil permeability | 1.2 | 1.13 | 1.2 | 1.2 | |
Temperature coefficient of Br, alpha | (%/℃) | -0.1 | -0.15 | -0.1 | -0.1 |
Required magnetizing field for saturation, Hs | (kA/m) | ≧1592 | ≧1990 | ≧1592 | ≧1592 |
(kOe) | (≧20) | (≧25) | (≧20) | (≧20) | |
Density | (Mg/m3) | 4.2 ~ 4.9 | 5.0 ~ 5.5 | 5.0 ~ 5.5 | 5.0 ~ 5.5 |
(g/cm3) | |||||
Method of forming | Injection mold |
NPI-9L (NC-9L) |
NPI-6LR (NC-6LR) |
NPI-6SR | NPI-7LR | NPI-7SR | ||
---|---|---|---|---|---|---|
Remanence, Br | (mT) | 640 ~ 720 | 480 ~ 560 | 460 ~ 520 | 550 ~ 610 | 520 ~ 580 |
(kG) | (6.4 ~ 7.2) | (4.8 ~ 5.6) | (4.6 ~ 5.2) | (5.5 ~ 6.1) | (5.2 ~ 5.8) | |
Coercivity, HCB | (kA/m) | 398 ~ 462 | 302 ~ 366 | 310 ~ 374 | 366 ~ 414 | 350 ~ 398 |
(kOe) | (5.0 ~ 5.8) | (3.8 ~ 4.6) | (3.9 ~ 4.7) | (4.6 ~ 5.2) | (4.4 ~ 5.0) | |
Intrinsic Coercivity, HCJ | (kA/m) | 637 ~ 796 | 637 ~ 796 | 835 ~ 1075 | 637 ~ 769 | 836 ~ 1075 |
(kOe) | (8.0 ~ 10.0) | (8.0 ~ 10.0) | (10.5 ~ 13.5) | (8.0 ~ 10.0) | (10.5 ~ 13.5) | |
Maximum energy product, (BH)max | (kJ/m3) | 68 ~ 76 | 36 ~ 48 | 37 ~ 45 | 52 ~ 60 | 47 ~ 56 |
(MGOe) | (8.5 ~ 9.5) | (4.5 ~ 6.0) | (4.6 ~ 5.6) | (6.5 ~ 7.5) | (5.9 ~ 7.0) | |
Recoil permeability | 1.2 | 1.2 | 1.13 | 1.2 | 1.13 | |
Temperature coefficient of Br, alpha | (%/℃) | -0.1 | -0.1 | -0.13 | -0.1 | -0.13 |
Required magnetizing field for saturation, Hs | (kA/m) | ≧1592 | ≧1592 | ≧1592 | ≧1592 | ≧1592 |
(kOe) | (≧20) | (≧20) | (≧20) | (≧20) | (≧20) | |
Density | (Mg/m3) | 4.6 ~ 5.1 | 4.6 ~ 5.1 | 5.5 ~ 6.0 | 5.0 ~ 5.5 | 5.0 ~ 5.5 |
(g/cm3) | ||||||
Method of forming | Injection mold |
- (NC): Compound for Injection Molding
- R: Heat resistant
- SR: Super Heat resistant
- This table shows measurement data byDaido's standard test pieces and not guranteed values.
- Moreover, since the above mentioned value is varied depending on magnet shape, its dimensions, test conditions and equipments. It is recommended that the fiqures be certified in actual products.
- The guarantee value would be consulted and set by the shape & size.
- The contents of data may change without prior notice.
Physical & mechanical properties
NEOQUENCH-P is a series of NdFeB bonded magnets using certain polymers as a binder. When exposed to heat, physical, mechanical, or dimensional changes may occur. Please test the products in the specific environment before actual use.
Compression molded magnets
Physical & Mechanical property NP-8, 8L, 8SL
Item | Unit | NP-8,8L, NP-11,12L |
NP-8SR |
---|---|---|---|
Electric resistivity (JIS C2525) |
μΩ・m | 56 | 31 |
μΩ・cm | 5600 | 3100 | |
Thermal Expansion Coefficient (JIS K7179) |
10-6/℃ | 10 | 7 |
(30~100℃) | |||
Bending strength (JIS K7171) |
MPa | 52 | 52 |
(kgf/mm2) | 5.3 | 5.3 | |
Bending Modulus (JIS K7171) |
MPa | 10800 | 10800 |
(kgf/mm2) | 1100 | 1100 | |
Ring Crushing Strength (JIS Z2507) |
MPa | 54 | 54 |
(kgf/mm2) | 5.5 | 5.5 |
Injection molded magnets
Physical & Mechanical property NPI-6, 6L, 6SR
Item | Unit | NPI-4L,6L, NPI-6,8L,9L |
NPI-6SR,6LR NPI-7SR,7LR |
---|---|---|---|
Electric resistivity (JIS C2525) |
μΩ・m | 130 | 130 |
μΩ・cm | 13000 | 13000 | |
Thermal Expansion Coefficient (JIS K7179) |
10-6/℃ | 26 | 21 |
(30~100℃) | |||
Bending strength (JIS K7171) |
MPa | 74 | 71 |
(kgf/mm2) | 7.6 | 7.2 | |
Bending Modulus (JIS K7171) |
MPa | 15700 | 24200 |
(kgf/mm2) | 1600 | 2470 | |
Ring Crushing Strength (JIS Z2507) |
MPa | 50 | 50 |
(kgf/mm2) | 5.1 | 5.1 | |
Hardness (JIS K7202) |
HRM | 70 | 107 |
Tensile Strength (JIS K7113) |
MPa | 37 | 33 |
(kgf/mm2) | 3.8 | 3.4 | |
Young's modulus (JIS K7113) |
MPa | 16000 | 25000 |
(kgf/mm2) | 1630 | 2550 |
Examples of overmolding and insert molding
- Overmolding NEOQUENCH-P to the shaft or yoke material
- Overmolding or insert molding of NEOQUENCH-P to pressed parts or high end resin parts.
- Compression molding NEOQUENCH-P with high end resin parts.
- Overmolding or insert molding high end resin to compression molded NEOQUENCH-P and shafts and other parts.